Radome and mechanical design

A radome is the product housing or plastic cover in front of the radar that protects it from mechanical impact and weather, see Figure 96. When designed correctly, the radome is effectively transparent to the radar signal and thus not impacting the radiated performance.

Transmission and reflection

When an electromagnetic (EM) wave hits the interface between two dielectrics, such as plastic and air, reflection and refraction occur at the boundary. Inside the dielectric, the propagation speed and wavelength change depending on the material’s permittivity. If the wavelength in free space is \(\lambda_{0}\), 5 mm at 60 GHz, the wavelength inside the material is \(\lambda=\frac{\lambda_{0}}{\sqrt{\varepsilon_r}}\), where \(\varepsilon_r\) is the relative dielectric constant of the material.

In the case of linearly polarized propagation at normal incidence, the Fresnel equations relate the ratio between the incident and transmitted fields:

(40)\[r=\frac{Z_{2} - Z_{1}}{Z_{2} + Z_{1}}, \quad t=\frac{2Z_{2}}{Z_{2}+Z_{1}},\]

where \(Z_{1}\) and \(Z_{2}\) are the corresponding wave impedances. The transmission and reflection factors are also related by \(t = 1 + r\). In most cases, we have non-magnetic materials so that \(Z = \sqrt{\frac{\mu_{r}}{\varepsilon_r}} = \frac{1}{\sqrt{\varepsilon_r}}\). An important special case is normal incidence between air and a dielectric. The reflection coefficient then simplifies to

(41)\[r=\frac{1 - \sqrt{\varepsilon_r}}{1 + \sqrt{\varepsilon_r}}\]

From this expression, we can see that the materials with a higher dielectric constant produce stronger reflections of the incidence signal. Conductors, such as metal, have a very high dielectric constant (\(\varepsilon_r \rightarrow \infty\)) and thus produce a strong reflection. Most polymers have a dielectric constant in the range 2–4, and therefore give a weaker reflection.

Radomes

Radome thickness

Let \(d_1\) be the distance to the radome, \(d_2\) the thickness, \(r_1\) and \(r_2\) the reflection coefficients, and \(t_1\) and \(t_2\) the corresponding transmission coefficients according to Figure 96. As an incident wave hits the first interface, a reflection \(r_1\), and a transmission \(t_1\) occur. Note that \(r_1 < 1\), so the reflected wave is out of phase with the incident wave. At the second interface, another reflection \(r_2\) and transmission \(t_2\) take place. With air on both sides of the dielectric, note from Eq. 40 that \(r_1 = -r_2\). The total reflection coefficient \(\Gamma_1\) then becomes [1]:

(42)\[\Gamma_{1}=\frac{r_{1} \left(1 - e^{-2jkd_{2}}\right)}{1 - r_{1}^{2} e^{-2jkd_{2}}}\]

where \(k = 2\pi/\lambda\) is the wave number in the material. Two notable special cases follow:

• For \(d_{2} = m\frac{\lambda}{2}, \; m = 1,2,...\) we have \(e^{-2jk d_{2}}=1\) and \(\Gamma_{1} = 0\).

• For \(d_{2} = m\frac{\lambda}{4}, \; m = 1,3,5,...\) we have \(e^{-2jk d_{2}}=-1\) and \(\Gamma_{1} = \frac{2r_{1}}{1+r_{1}^{2}}\).

The optimum radome thickness occurs when the dielectric is perfectly reflectionless, i.e. when the thickness is a multiple of half a wavelength. This can also be understood from the fact that the round trip of the wave inside the radome introduces a 360° phase shift, thereby cancelling the reflected wave \(r_{1}\).

Figure 96 Transmitted and reflected signals from a half-wavelength radome. Secondary reflections have been omitted for simplicity.

As an example, if the material is polycarbonate with relative permittivity \(\varepsilon_r=2.75\), the optimal radome thickness becomes:

(43)\[d_{2}=m\frac{\lambda}{2} = m\frac{\lambda_{0}}{2\sqrt{\varepsilon_r}} = m\frac{5}{2\sqrt{2.75}} \approx m \times 1.51 \:\mathrm{mm}, m = 1,2,...\]

If the dielectric thickness is an odd multiple of \(\frac{\lambda}{4}\), maximum reflection occurs. The relative dielectric constant of some more materials can be found in Table 32.

Dielectric constant of common materials

The dielectric constant of some common polymers at 60 GHz is presented in Table 32.

Table 32 Relative permittivity of common materials [2]

Material	Re(\(\varepsilon\)) at 60 GHz
Acrylic glass	2.5
Alumina	9.3
Fused Quartz	3.8
MACOR	5.5
PEEK	3.12 [3]
PMMA	2.6 [4]
Polycarbonate (PC)	2.75 [4] [5]
Polyethylene (PE)	2.3 [5] [6] [7] [8]
Polypropylene (PP)	2.2 [5] [8]
Polystyrene (Rexolite)	2.5
PTFE (Teflon)	2.05 [5]

Footnotes

[1]

S. J. Orfanidis, Electromagnetic Waves and Antennas, New Jersey: Rutgers University, 2016.

[2]

S. R. Artem Boriskin, Aperture Antennas for Millimeter and Sub-Millimeter Wave Applications, Springer, 2017.

[3]

N. C. F. T. V. et al., “Complex Dielectric Permittivity of Engineering and 3D-Printing Polymers at Q-Band,” J. Infrared Milli Terahz Waves, vol. 39, pp. 1140–1147, 2018.

[4] (1,2)

B. L. G. et al., “A Comparison of Measurements of the Permittivity and Loss Angle of Polymers in the Frequency Range 10 GHz to 90 GHz,” 2021 15th European Conference on Antennas and Propagation (EuCAP), pp. 1–5, 2021.

[5] (1,2,3,4)

Y. O. K. F. M. M. K. S. Yuka Hasegawa, “Complex Permittivity Spectra of Various Insulating Polymers at Ultrawide-Band Frequencies,” Electrical Engineering in Japan, vol. 198, no. 3, pp. 11–18, 2017.

[6]

10. 23. Lamb, Miscellaneous Data on Materials for Millimetre and Submillimetre Optics.

[7]

Salski et al., “Complex Permittivity of Common Dielectrics in 20–110 GHz Frequency Range Measured with a Fabry–Perot Open Resonator.”

[8] (1,2)

Afsar et al., “A New 60 GHz Open-Resonator Technique for Precision Permittivity and Loss-Tangent Measurement.”